Catalog - Ceramic flux

FSA ChTA 650-20/80

Minimal amount of order – 10000 kg
Basicity
1,2
Bulk density, kg/dm³
0,95-1,2
Grain size (EN ISO 14174), mm
0,3-2,0
Slag crystallization rate
Average
Current and polarity
AC, DC+
Alloyage
Si – low, Mn – average
Baking modes
325±25 ◦С, 2-4 hours
Send a request
Overview
Mechanical properties
Classification EN ISO
Chemical composition
Total oxides Al2O3 + CaO + MgO Al2O3 CaF2
% min. 40 min. 20 min.  22
Accompanying documents
№АЦСМ-62-00480 ФСА (ТУ КЕРАМАКС)
№АЦСМ-62-00481 ФСА (ТУ ЧТПЗ)
Description
FSA CT A 650-20/80 is specifically designed for the production of longitudinal and spiral welded pipes. The flux slightly alloys the deposited metal with silicon (Si) and manganese (Mn) and performs equally well with both direct and alternating current. This flux ensures a slight reinforcement of the weld seam when welding longitudinal joints of pipes at high welding speeds.

Due to careful metallurgical calculations, FSA CT A produces deposited metal without hard inclusions. It can be used for welding all types of pipe steels, up to strength class X100, providing high impact toughness values.

Wire grade

Chemical composition

Mexchanical properties

C

Mn

Si

P

S

Ni

Мо

σт
N/mm2

σв
N/mm2

δ [%]

T [°C]

KCV [J/sm2]

KCU [J/sm2]

S2Mo

0,07

1,20

0,42

0,02

0,01

0,03

0,47

600

660

≥18

-20

80

-

-40

45

-

-60

-

-

S3MoTiB

0,07

1,34

0,59

0,02

0,01

0,01

0,48

630

680

-20

100

-

-40

80

-

-60

-

-

Cв-08ГА

0,07

1,10

0,32

0,02

0,01

0,10

0,013

460

530

≥25

-20

60

-

-40

40

-

-60

-

-

SA AB 1 AC H5:

S

designed for flux-cored arc welding

A

agglomerated flux

AB

aluminate-basic type

1

designed for welding carbon, low-alloy, and high-strength structural steels

AC

welding with direct and alternating current

H5

the maximum allowable content of diffusible hydrogen is less than 5.0 ml per 100 g of deposited metal