UF-K

Minimum delivery batch - 10 tons

Basic capacity (by Bonishevsky)

1,2

Bulk density, kg/dm3

1,0-1,3

Grain size (EN ISO 14174), mm

0,25-2,0

Annealing modes

250-350°С, 2 hours

General description

Mechanical properties

Classification of EN ISO

Chemical composition

Total oxides	Al₂O₃ + CaO + MgO	Al₂O₃	CaF₂
%	minimum 40	minimum 20	minimum 22

Support documentation

Description

UF-K agglomerated neutral flux. It is designed for mechanized arc welding and surfacing of carbon and low-alloy steels with low-carbon and alloy welding wire. It provides good welding and technological properties when welding both single-pass and multi-pass welds. It is recommended for welding structures with no increased requirements for impact strength

Wire grade	Chemical composition							Mechanical Properties
	C	Si	Mn	Cr	Ni	Mo	Nb	Yield strength N/mm2	Breaking strength N/mm2	δ [%]	T [°C]	KCV [J / cm2]	KCU [J / cm2]	Твердость, [HRCэ]
	C	Si	Mn	Cr	Ni	Mo	Nb	Yield strength N/mm2	Breaking strength N/mm2	δ [%]
Sv-08GA (Cв-08ГА)	0,06	0,50	1,20	0,15	0,20	-	-	minimum 450	minimum 500	minimum 20	-20	50		-

SA AB 1 AC H5:
S	is intended for submerged arc welding
A	agglomerated flux
AB	aluminate-basic type
1	intended for welding carbon, low-alloy and high-strength structural steels
AC	DC or AC welding
H5	maximum permissible diffusible hydrogen content is less than 5.0 ml per 100 g of weld metal