UF-S

Minimum delivery batch - 10 tons

Basic capacity (by Bonishevsky)

1,0

Bulk density, kg/dm3

1,0-1,3

Grain size (EN ISO 14174), mm

0,2-1,6

Alloying

Chromium compensating

Annealing modes

275-325°С, 2 hours

General description

Mechanical properties

Classification of EN ISO

Chemical composition

Total oxides	CaO + MgO + SiO₂	CaO + MgO
%	minimum 50	minimum 15

Support documentation

UF-S АЦСМ-62-00126

Description

UF-S is a neutral agglomerated chromium compensating flux. It is intended for automatic and semi-automatic welding of stainless, corrosion-resistant and heat-resistant steels with suitable welding wires and for arc strip cladding.

The flux is designed for direct current welding of single-pass seams without limiting the thickness of the parts to be welded. It shows good welding and technological characteristics.

It is used in the chemical and petrochemical industries, for pressure vessels, storage facilities and containers for chemical products, in solving problems of the energy and nuclear industries, the pulp and paper industry, civil engineering, transport engineering, etc.

Wire grade	Chemical composition							Mechanical Properties
Wire grade	C	Mn	Si	P	S	Ni	Мо	Yield strength N/mm2	Breaking strength N/mm2	δ [%]	T [°C]	KCV [J / cm2]	KCU [J / cm2]
Sv-Sv-05X20N9FBS (Св-05Х20Н9ФБС)	0,04	0,76	1,04	0,026	0,011	10,0	0,093	378	624	35	-20	120	-
											-40	112	-
											-50	101	-
											-60	-	140
Sv-07X25N13 (Св-07Х25Н13)	0,06	1,07	0,78	0,027	0,01	12,6	0,013	333	549	39	-20	127	-
											-40	127	-
											-50	124	-
											-60	-	152

SA CS 2 DC :
S	is intended for submerged arc welding
A	agglomerated flux
CS	calcium silicate type
2	It is intended for arc welding and surfacing of corrosion-resistant and heat-resistant steels and/or nickel and nickel-based alloys
DC	direct current welding